Title: Caracterização mecânica, estabilidade térmica e reação ao fogo do bambu mossô (L. Phyllostachys pubescens)
Other Titles: Mechanical characterization, thermal stability and reaction to fire and bamboo moso (L. Phyllostachys pubescens)
Author(s)/Inventor(s): Gomes, Bruno Menezes da Cunha
Advisor: Toledo Filho, Romildo Dias
Abstract: Esta pesquisa apresenta uma análise comportamental do bambu da espécie Phyllostachys pubescens sob cargas de compressão uniaxial e flexão em três pontos, além da sua reação ao fogo e seu comportamento sob altas temperaturas. Ensaios de resistência a compressão foram realizados em amostras com relação de aspecto (H/D) de 1, 2 e 3, em amostras sem nó e com 1 e 2 nós e em amostras saturadas e na condição de umidade de equilíbrio. Ensaios de flexão em três pontos foram realizados tanto em amostras saturadas quanto na umidade natural. O efeito da temperatura foi estudado realizando-se ensaios físicos e de tração direta em ripas de bambu antes e após exposição das mesmas às temperaturas de 100, 150, 200 e 250 ºC. Foi avaliada a influência da taxa de aquecimento (0,5 e 20 °C/min) e do tempo de exposições (15, 30, 60, 120 e 240 minutos) nas propriedades físicas e mecânicas residuais do bambu. A reação ao fogo foi avaliada realizando ensaios no cone calorímetro de perda de massa com um fluxo radiante de 50 kW/m². Os resultados obtidos indicaram que a até 100C há ganhos de resistência a tração, a geometria mais adequada para o ensaio de compressão uniaxial é 2DHSN e que a reação ao fogo do bambu é comparável às de madeiras.
Abstract: This research presents a behavioral analysis of Phyllostachys pubescens bamboo under uniaxial compression loads and three-point flexion, as well as its reaction to fire and its behavior under high temperatures. Compressive strength tests were performed on samples with an aspect ratio (H/D) of 1, 2 and 3, on knotless and 1 and 2 knot samples and on saturated samples at equilibrium humidity. Three point bending tests were performed on both saturated and natural moisture samples. The effect of temperature was studied by performing physical and direct tensile tests on bamboo slats before and after exposure to temperatures of 100, 150, 200 and 250 ºC. The influence of the heating rate (0.5 and 20 °C/min) and exposure time (15, 30, 60, 120 and 240 minutes) on the residual physical and mechanical properties of bamboo was evaluated. The reaction to fire was evaluated by conducting calorimeter cone tests with a radiant flux of 50 kW/m². The results indicated that at up to 100C there are tensile strength gains, the most suitable geometry for the uniaxial compression test is 2DHSN and that the reaction to fire of bamboo is comparable to that of wood.
Keywords: Bambu
Reação ao fogo
Temperatura
Sustentabilidade
Subject CNPq: CNPQ::ENGENHARIAS::ENGENHARIA CIVIL
Program: Programa de Pós-Graduação em Engenharia Civil
Production unit: Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia
Publisher: Universidade Federal do Rio de Janeiro
Issue Date: Jul-2019
Publisher country: Brasil
Language: por
Right access: Acesso Aberto
Appears in Collections:Engenharia Civil