| Title: | Avaliação da resistência mecânica e da molhabilidade de fibras de aramida após tratamento com plasma de argônio |
| Author(s)/Inventor(s): | Santos, Mariana Oliveira |
| Advisor: | Simão, Renata Antoun |
| Co-advisor: | Bastian, Fernando Luiz |
| Abstract: | Esse trabalho apresenta a análise da resistência mecânica, da molhabilidade e da morfologia da superfície de fibra de aramida tratada com plasma de argônio. A fibra foi tratada com plasma de argônio com vácuo de 8x10-1 bar com potência de 50 e 100 W, sendo que para cada potência foram realizados ensaios com duração de 1, 3 e 5 minutos. Os ensaios realizados foram ensaios de tração, tensiometria e microscopia eletrônica de varredura (MEV). Por meio da análise dos resultados, observou-se que, para o tratamento com 100 Watts, a fibra apresentou uma melhoria na sua molhabilidade além de um aumento de 47% na resistência da fibra para o tratamento com duração de 3 minutos e, para o tratamento com duração de 5 minutos, nota-se que o valor da resistência começa a decair. O tratamento com plasma também aumentou a rugosidade da superfície da fibra e causou a inclusão de incrustrações na mesma, indicando uma possível melhoria no intertravamento mecânico entre fibra e matriz. |
| Abstract: | This work presents the analysis of mechanical strength, wettability and the surface of aramid fiber treated with argon plasma. The fiber was treated with argon plasma with a vacuum of 8x10-1 bar with power of 50 and 100 Watts, and, for each voltage, tests were carried out with duration of 1, 3 and 5 minutes. The tests performed were tensile tests, tensiometry and scanning electron microscopy (SEM) By analyzing the results, it was observed that, for the 100 Watt treatment, the fiber presented an improvement in its wettability and an increase of 47% in the fiber’s strength resistance for the treatment duration of 3 minutes and, for the duration of 5 minutes, it is noticed that the value of the strength resistance begins to decay. The plasma treatment also increased the roughness of the fiber surface and caused the inclusion of incrustations on it, indicating a possible improvement in the mechanical interlock between fiber and matrix. |
| Keywords: | Engenharia metalúrgica e de materiais Fibras de aramida x avaliação. |
| Subject CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| Program: | Programa de Pós-Graduação em Engenharia Metalúrgica e de Materiais |
| Production unit: | Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia |
| Publisher: | Universidade Federal do Rio de Janeiro |
| Issue Date: | Apr-2017 |
| Publisher country: | Brasil |
| Language: | por |
| Right access: | Acesso Aberto |
| Appears in Collections: | Engenharia Metalúrgica e de Materiais |