Title: Recuperação hidrometalúrgica de cobre e zinco a partir de cinzas de fundição de latão utilizando extração por solventes com D2EHPA
Author(s)/Inventor(s): Martins, Júlia Mont’Alverne
Advisor: Dutra, Achilles Junqueira Bourdot
Co-advisor: Mansur , Marcelo Borges
Abstract: Uma amostra composta de cinzas de fundição de latão foi processada por lixiviação e extração por solventes visando à separação de zinco e cobre, elementos predominantes na amostra, 48% de zinco e 16,6% de cobre. O estudo foi realizado em escala de bancada e piloto, utilizando-se ácido sulfúrico como agente lixiviante e D2EHPA como agente extratante. Os seguintes parâmetros operacionais foram estudados na etapa de extração por solventes: tempo, pH, concentração de D2EHPA, razão A/O na etapa de extração e razão O/A na etapa de reextração. O zinco foi lixiviado eficientemente por H2SO4 (rendimento de 91,9%), enquanto apenas 8,6% do cobre foi lixiviado, bem como extraído seletivamente frente ao cobre na etapa de extração por solventes. Foi realizada uma corrida de extração por solventes contínua em escala piloto utilizando-se 4 estágios de extração (pH 2 e razão A/O = 1) e 2 estágios de reextração (razão O/A = 2), obtendo-se um rendimento de extração de zinco de 91,8% e de reextração de 96,9%. O rendimento de extração do ferro foi de 85,9%, evidenciando a necessidade de sua remoção prévia se requerida. A extração do flúor foi de 29,9% e a de cloro foi 10,4%, tendo sido observada extração destas espécies conjuntamente com ferro e zinco, respectivamente. Como o cobre não foi lixiviado eficientemente com ácido sulfúrico, obteve-se um concentrado de cobre contendo 42,2%.
Abstract: A blend of brass ashes sample was processed through leaching and solvent extraction aiming to separate zinc and copper, the predominant species found in the residue, i.e., 48% of zinc and 16.6% of copper. The present study was performed in bench and pilot scales using sulfuric acid as leaching agent and D2EHPA as extracting agent. The following operating parameters were evaluated in the solvent extraction step: time, pH, D2EHPA concentration, A/O ratio in the extraction step and O/A ratio in the stripping step. Zinc present in the brass ashes was efficiently leached by H2SO4 (recovery of 91.9%), whereas only 8.6% of copper was leached, as well as selectively extracted over copper by solvent extraction with D2EHPA. A continuous solvent extraction run in pilot scale was carried out using 4 extraction stages (pH = 2, A/O ratio = 1) and 2 stripping stages (O/A ratio = 2), where 91.8% of zinc extraction and 96.9% of zinc stripping were achieved. Iron extraction efficiency reached 85.9%, thus evidencing the need for previous removal if required. The fluorine extraction was 29.9% and that for chlorine was 10.4%, whose extractions are related to iron and zinc extractions, respectively, as evidenced by species speciation analysis. As copper was not efficiently leached by sulfuric acid, a copper concentrate containing 42.2% was produced.
Keywords: Engenharia metalúrgica e de materiais
Extração por solventes
Cinzas de latão
Subject CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Program: Programa de Pós-Graduação em Engenharia Metalúrgica e de Materiais
Department : Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia
Publisher: Universidade Federal do Rio de Janeiro
Issue Date: Sep-2017
Publisher country: Brasil
Language: por
Right access: Acesso Aberto
Appears in Collections:Engenharia Metalúrgica e de Materiais

Files in This Item:
File Description SizeFormat 
876831.pdf2,42 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.