Author(s)/Inventor(s): Bendinelli, Elber Vidigal
Advisor: Margarit-Mattos, Isabel Cristina Pereira
Co-advisor: Aoki, Idalina Vieira
Abstract: O objetivo dessa tese foi desenvolver partícula de hidróxido duplo lamelar (HDL) com ação inteligente sobre a corrosão de aço carbono e testar seu desempenho como pigmento anticorrosivo em tinta epóxi. A metodologia consistiu de quatro etapas: i) avaliação da eficiência anticorrosiva e seleção do inibidor de corrosão; ii) síntese de HDLs dopados com inibidor; iii) formulação e caracterização do desempenho de revestimentos pigmentados com HDLs e iv) estudo da cinética de liberação do inibidor pelos HDLs sintetizados. Na primeira etapa, o imidazol foi selecionado por suas características moleculares. Na segunda etapa, dois HDLs foram sintetizados por reconstrução lamelar: HTC-Im e HTCTe-Im. O HTC-Im apresentou maior cristalinidade segundo a DRX, enquanto HTCTe-Im se caracterizou por liberação de maior quantidade de imidazol, com cinética mais rápida, conforme caracterização por espectroscopia UV-Vis. Por esse motivo, HTCTe-Im foi escolhido para ser adicionado como pigmento em tinta epóxi. Na terceira etapa, o desempenho em ensaios de corrosão não apontou vantagens claras no uso do pigmento HTCTe-Im. Na quarta etapa de trabalho se procedeu a caracterização das propriedades de troca iônica e o mecanismo de liberação do inibidor por HTCTe-Im e HTC-Im. Foi verificado que a mistura HTCTe-Im + HTC-Im apresentou sinergia interessante, o HTCTe-Im liberou mais rápido e maior quantidade de imidazol. Já o HTC-Im capturou maior quantidade de cloreto através do mecanismo de troca iônica.
Abstract: The objective of this thesis was to develop layered double hydroxide (LDH) particles with smart action against steel corrosion and to test its performance as pigment in epoxy paint. The methodology consisted of four steps: i) evaluation of anti-corrosion efficiency and selection of corrosion inhibitors; ii) synthesis of inhibitor doped LDH; iii) formulation and performance characterization of LDH pigmented coatings; and iv) study of inhibitor release kinetics by synthesized LDHs. In the first stage, imidazole was selected for its molecular characteristics. In the second stage, two LDHs were synthesized by lamellar reconstruction: HTC-Im and HTCTe-Im. HTC-Im showed higher crystallinity according to XRD, while HTCTe-Im was characterized by the release of a larger amount of imidazole, with faster kinetics, characterized by UV-Vis spectroscopy. For this reason, HTCTe-Im was chosen to be added as pigment in an epoxy paint. In the third step, the performance in the corrosion tests did not point to clear advantages when using HTCTeIm pigment. In the fourth stage, the characterization of the ion exchange properties and the inhibitor release mechanism by HTCTe-Im and HTC-Im were performed. The HTCTe-Im + HTC-Im mixture was found to show interesting synergy, HTCTe-Im released faster and higher amounts of imidazole. HTC-Im has captured more chloride through the ion exchange mechanism.
Keywords: Hidróxido duplo lamelar
Revestimentos inteligentes
Cinética de liberação
Imidazol
Subject CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Program: Programa de Pós-Graduação em Engenharia Metalúrgica e de Materiais
Production unit: Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia
Publisher: Universidade Federal do Rio de Janeiro
Issue Date: Oct-2019
Publisher country: Brasil
Language: por
Right access: Acesso Aberto
Appears in Collections:Engenharia Metalúrgica e de Materiais

Files in This Item:
File Description SizeFormat 
ElberVidigalBendinelli.pdf8,08 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.