| Título : | Efeito do envelhecimento e da geração de “whitening” no comportamento mecânico do PVDF |
| Autor(es)/Inventor(es): | Barros Junior, Edwilson Moreira de |
| Tutor: | Costa Neto, Célio Albano da |
| Tutor : | Costa., Marysilvia Ferreira da |
| Resumen: | O polifluoreto de vinilideno(PVDF) é um polímero com elevada resistência química e mecânica e, por este motivo, está sendo amplamente utilizado na composição de linhas flexíveis aplicadas na produção de petróleo offshore, agindo como uma camada de estanqueidade. A ocorrência de whitening é frequentemente observada no PVDF, sendo este caracterizado pela formação de regiões esbranquiçadas e que está associado ao processo de cavitação (formação de microvazios). Este trabalho tem como objetivo o estudo do efeito do envelhecimento em petróleo do PVDF em 30, 90 e 180 dias a 80 °C e da geração de whitening que foi gerado através de ensaios de tração por carregamento cíclico. Corpos de prova foram envelhecidos em petróleo antes e após a geração do efeito whitening e para fins comparativos um grupo de corpos de prova não sofreu a geração de whitening, apenas foram envelhecidos. Para avaliação do comportamento mecânico foram realizados ensaios de tração e para análise da cristalinidade foram utilizadas técnicas de difração de raios X, calorimetria exploratória diferencial e espectroscopia de infravermelho. |
| Resumen: | The polyvinylidene (PVDF) is a polymer with high chemical and mechanical resistence, for this reason is being largely used in the composition of flexible pipes used in petroleum production offshore, acting as sealing layer. One effect named whitening can appear in the material, being characterized by the formation of whitened regions and is associated with cavitation process (growth of microvoids). This work has the objective of studying the effect of PVDF aging in petroleum during 30, 90 and 180 days at 80 ° C and the generation of whitening that was generated by traction tests by cyclic loading. Test specimens were aged in petroleum before and after the generation of the whitening effect and for comparative purposes a group of specimens did not undergo generation of whitening, just been aged. To evaluate the mechanical behavior, tensile tests were carried out and X-ray diffraction, differential scanning calorimetry and infrared spectroscopy were used for crystallinity analysis. |
| Materia: | Engenharia metalúrgica e de materiais Envelhecimento Polifluoreto de vinilideno(PVDF) |
| Materia CNPq: | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
| Programa: | Programa de Pós-Graduação em Engenharia Metalúrgica e de Materiais |
| Unidade de producción: | Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia |
| Editor: | Universidade Federal do Rio de Janeiro |
| Fecha de publicación: | oct-2017 |
| País de edición : | Brasil |
| Idioma de publicación: | por |
| Tipo de acceso : | Acesso Aberto |
| Aparece en las colecciones: | Engenharia Metalúrgica e de Materiais |
Ficheros en este ítem:
| Fichero | Descripción | Tamaño | Formato | |
|---|---|---|---|---|
| 871948.pdf | 833.94 kB | Adobe PDF | Visualizar/Abrir |
Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.