Título : Investigação do comportamento de um aditivo para óleos lubrificantes por meio de ensaios tribológicos e técnicas de caracterização de nanomateriais
Autor(es)/Inventor(es): Freitas, Guilherme Teixeira de.
Tutor: Oliveira, Sylvio José Ribeiro de
Tutor : Camargo Junior, Sérgio Alvaro de Souza
Resumen: Este trabalho teve por objetivo investigar experimentalmente o desempenho de um aditivo comercial de óleos lubrificantes que promete reduzir o coeficiente de atrito a partir do polimento superficial na escala nanométrica, devido à ação de nanopartículas sintetizadas durante o processo de desgaste. Foram realizados ensaios tribológicos em um tribômetro rotativo nas configurações quatro esferas e pino-disco, utilizando dois óleos básicos de viscosidades distintas (27cSt e 107cSt à temperatura de 40ºC). Foram comparados os resultados de desgaste, coeficiente de atrito e rugosidade superficial dos ensaios sem aditivo e com aditivo. Técnicas de caracterização de nanomateriais (MEV, EDS, espectroscopia Raman e AFM) foram utilizadas para a obtenção de análises mais aprofundadas das superfícies após os ensaios. Os efeitos do aditivo sobre os aspectos tribológicos se mostraram dependentes das condições de ensaio, sendo que os melhores resultados (redução conjunta de desgaste, coeficiente de atrito e rugosidade) foram obtidos para os ensaios com o óleo de maior viscosidade (107cSt). As técnicas de caracterização de nanomateriais empregadas forneceram mais informações sobre as superfícies ensaiadas, mas não permitiram encontrar evidências conclusivas da deposição de nanopartículas sintetizadas pelo aditivo.
Resumen: This research had the purpose of investigating experimentally a comercial additive of lubricating oils which promises to reduce the friction coefficient by the surface polishment at the nanometric scale, due to the action of nanoparticles synthetized during the wear process. Tribological tests were conducted on a rotative tribometer at the fourball and pin-on-disc configurations, using two basic oils with different viscosities (27cSt and 107cSt at the temperature of 40ºC). The results of wear, friction coefficient and surface rugosity for the tests with and without additive were compared. Nanomaterials characterization techniques (SEM, EDS, Raman spectroscopy and AFM) were used in order to provide a deeper analysis of the surfaces after the tests. The effects of the additive over the tribological aspects depended on the tests conditions, and the best results (reduction of wear, friction coefficient and rugosity) were observed for the tests with the oil of higher viscosity (107 cSt). The nanomaterials characterization techniques provided more information about the surfaces tested, but they didn’t allow to find conclusive evidences of the deposition of nanoparticles synhtetized by the additive.
Materia: Lubrificantes
Pino-Disco
Materia CNPq: CNPQ::ENGENHARIAS::ENGENHARIA MECANICA
Programa: Programa de Pós-Graduação em Engenharia Mecânica
Unidade de producción: Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia
Editor: Universidade Federal do Rio de Janeiro
Fecha de publicación: jun-2018
País de edición : Brasil
Idioma de publicación: por
Tipo de acceso : Acesso Aberto
Aparece en las colecciones: Engenharia Mecânica

Ficheros en este ítem:
Fichero Descripción Tamaño Formato  
GuilhermeTeixeiraDeFreitas.pdf7.31 MBAdobe PDFVisualizar/Abrir


Los ítems de DSpace están protegidos por copyright, con todos los derechos reservados, a menos que se indique lo contrario.