Title: Produção, caracterização e avaliação in vitro de filmes finos de vidro niobo-fosfato por deposição a laser pulsado
Author(s)/Inventor(s): Sanz, Carolina Kaminski
Advisor: Camargo Júnior, Sérgio Álvaro de Souza
Co-advisor: Santos, Aline Raybolt dos
Abstract: A osteointegração dos implantes está relacionada com a capacidade da superfície do implante realizar ligações químicas diretas e fortes com o tecido ósseo adjacente. Tratamentos de superfície dos implantes são alternativas para conferir essas propriedades superficiais, dentre os quais se destacam os recobrimentos com materiais bioativos. Nesse trabalho foram sintetizados filmes finos de biovidro fosfatado com nióbio (CaF2-CaO-Nb2O5-P2O5) em substratos de titânio visando à indução de bioatividade e a melhora na sua osteointegração. Os filmes foram depositados por pulsed laser deposition (PLD) e analisados por MEV, EDS, XPS, DRX, FRX, AFM, perfilometria, scratch test, contato focal, proliferação e diferenciação celular. Nas análises por XPS foram encontradas estruturas de CaNb2(P2O6) e NbOx. Não foram identificadas fases cristalinas nos filmes, por se tratar de um material com estrutura amorfa. Em conjunto, os resultados indicam que a síntese do material e a deposição são reprodutivas: foi possível depositar filmes finos de vidro bioativo em titânio por PLD, houve transferência estequiométrica do alvo para os filmes e, após a deposição, o material permaneceu com sua estrutura vítrea. Os ensaios in vitro não revelaram diferenças estatisticamente significantes entre os filmes e o controle, apesar dos filmes depositados com 50 mJ apresentarem um aumento na quantidade celular e os filmes de 100 mJ apresentarem melhor espalhamento celular.
Abstract: Implant osseointegration is related to the implant surface’s ability to create strong and direct chemical bonds with adjacent bone tissue. Surface treatments are a way to obtain these surface properties. Among the different treatments, bioactive materials coatings stand out. In this work, thin niobo-phosphate bioactive glass (CaF2-CaONb2O5-P2O5) films were deposited by pulsed laser deposition (PLD) on Ti substrates aiming to enhance its bioactivity and osseointegration. Samples were analyzed by SEM, EDS, XPS, XRD, XRF, AFM, profilometry, scratch test, focal contact and cell proliferation and differentiation. In XPS analysis, CaNb2(P2O6) and NbOx structures were found. Crystalline phases were not identified on the films, since the glass has an amorphous structure. Together, these results suggest that both material synthesis and deposition are reproducible. It was possible to deposit thin bioactive glass films on titanium by PLD, there was stoichiometric transfer from the target to the films and, after the deposition, the material’s glassy structure was maintained. In vitro tests did not reveal statistically significant differences between deposited films and the Ti control samples, even though samples deposited with 50 mJ showed an increase in cell quantity, and samples deposited with 100 mJ presented better cell spreading.
Keywords: Engenharia metalúrgica e de materiais
Vidros bioativos
Osteointegração
Subject CNPq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
Program: Programa de Pós-Graduação em Engenharia Metalúrgica e de Materiais
Production unit: Instituto Alberto Luiz Coimbra de Pós-Graduação e Pesquisa de Engenharia
Publisher: Universidade Federal do Rio de Janeiro
Issue Date: Apr-2017
Publisher country: Brasil
Language: por
Right access: Acesso Aberto
Appears in Collections:Engenharia Metalúrgica e de Materiais

Files in This Item:
File Description SizeFormat 
872191.pdf1,54 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.